Copper plated steel wire:
Mainly using 70# (C72DA) high-quality wire rod, which has been pre-treated, rough drawn, heat treated, fine drawn, and drawn to 0.5mm-1.2mm steel wire, and then passed through a tempering lead pot for electroless copper plating, and the surface of the steel wire is covered with a layer of high toughness.The main product is low-tin bronze, with a golden or pink surface. It has excellent high strength and is used to make rubber hoses, telescopic tubes, steel mesh skeleton polyethylene composite pipes, and is a reinforcing material for composite pipe skeletons.
Steel wire mesh composite pipe steel wire quality standards | ||||||||
NameName | Diameter | Breaking forceBreaking Iorce | Tensile strength | Elongation at break Frte | Wield ratio | Twist | Copper layer weight CCDPT welght | |
UnitUnit | mm | N | MPa | % | % | 次 | g/kg | |
quality standards | 0.5±0.02 | ≥400 | ≥2100 | ≥5 | 285 | 250 | 0.3~1.0 | |
0.6±0.02 | 2550 | ≥2050 | 25 | ≥85 | 250 | 0.3~1.0 | ||
0.7±0.02 | ≥750 | 22050 | ≥5 | ≥85 | ≥50 | 0.3~1.0 | ||
0.8±0.02 | 21030 | ≥2050 | ≥5 | ≥85 | ≥50 | 0.3~1.0 | ||
0.9±0.02 | ≥1300 | 22050 | 25 | 285 | 250 | 0.3~1.0 | ||
1.0±0.02 | ≥1450 | ≥1950 | ≥5 | ≥85 | ≥22 | 0.3~1.0 | ||
1.2±0.02 | 22035 | ≥1850 | ≥5 | ≥85 | ≥22 | 0.3~1.0 | ||
Note: Special requirements are subject to negotiation between the supply and demand parties. | ||||||||
Copper plated steel wire:
Mainly using 70# (C72DA) high-quality wire rod, which has been pre-treated, rough drawn, heat treated, fine drawn, and drawn to 0.5mm-1.2mm steel wire, and then passed through a tempering lead pot for electroless copper plating, and the surface of the steel wire is covered with a layer of high toughness.The main product is low-tin bronze, with a golden or pink surface. It has excellent high strength and is used to make rubber hoses, telescopic tubes, steel mesh skeleton polyethylene composite pipes, and is a reinforcing material for composite pipe skeletons.
Steel wire mesh composite pipe steel wire quality standards | ||||||||
NameName | Diameter | Breaking forceBreaking Iorce | Tensile strength | Elongation at break Frte | Wield ratio | Twist | Copper layer weight CCDPT welght | |
UnitUnit | mm | N | MPa | % | % | 次 | g/kg | |
quality standards | 0.5±0.02 | ≥400 | ≥2100 | ≥5 | 285 | 250 | 0.3~1.0 | |
0.6±0.02 | 2550 | ≥2050 | 25 | ≥85 | 250 | 0.3~1.0 | ||
0.7±0.02 | ≥750 | 22050 | ≥5 | ≥85 | ≥50 | 0.3~1.0 | ||
0.8±0.02 | 21030 | ≥2050 | ≥5 | ≥85 | ≥50 | 0.3~1.0 | ||
0.9±0.02 | ≥1300 | 22050 | 25 | 285 | 250 | 0.3~1.0 | ||
1.0±0.02 | ≥1450 | ≥1950 | ≥5 | ≥85 | ≥22 | 0.3~1.0 | ||
1.2±0.02 | 22035 | ≥1850 | ≥5 | ≥85 | ≥22 | 0.3~1.0 | ||
Note: Special requirements are subject to negotiation between the supply and demand parties. | ||||||||